Home > Product > Ceramic Foam Filter > Zirconia Ceramic Coam Filter For Steel and Alloy

Zirconia Ceramic Coam Filter For Steel and Alloy

Zirconia Ceramic Foam Filters are used for molten all types of steel like unalloyed, low alloyed, stainless and high-alloyed.

Filters are recommended especially for high quality grades of alloys.

With their excellent resistance to attack and corrosion from molten steel liquid, they can effectively remove inclusions, reduce trapped gas from liquid metal and provide laminar flow, and then the filtered metal is significantly cleaner.

Cleaner metal results in higher-quality castings, less scrap, and fewer inclusion defects. They are the best choice for filtering of determined for filtering of steel and steel alloys up to the temperature of 1700℃.

Inquire Now Next Product

Parameter

Zirconia Ceramic Foam Filter have good resistance to attack and corrosion of liquid steel, can effectively remove inclusions in liquid metal, reduce trapped gas in liquid metal, and provide laminar flow, so that the filtered metal is significantly clean.

Zirconia ceramic foam filters are the best choice for filtering of determined for filtering of steel and steel alloys up to the temperature of 1700℃. Filters are recommended especially for high quality grades of alloys.

Zirconia Ceramic Coam Filter For Steel and Alloy

Advantages:

● Good filtration capacity

● Ideal for the filtration of high alloyed steel

● Filters can be preheated for investment casting application

● Improve casting qualification rate

● Improve the casting metallographic structure

Type	Zirconia ceramic foam filter for steel and alloy
Color	Yellow
PPI	10-40PPI(PPI=pores per inch)
Work Temperature	≤1700℃
Porosity	80-90%
Bulk Density	0.8-1.5g/cm3
Compressive strength	≥1.5Mpa(Room temperature)
ZrO2(%)	85-90
Al2O3 (%)	5-10
SiO2(%)	≤4
MgO(%)	4-5
Thermal shock resistance (Times/1100°C)	6
Certificate	ISO9001:2015

Application:

Filtration of molten steel and alloy

Filtration of large scale iron casting

Filtration of high quality grades of alloys

Preheated for investment casting application